Barsham Nickel Alloys is a prominent Doha, Qatar-based manufacturer and supplier of high-grade metal alloys such as Haynes 25 (L605) foil. Being renowned for superior strength, corrosion resistance, and high-temperature properties, Haynes 25 is used in aerospace, chemical, and industrial applications on a large scale. With the motive of providing the best products, Barsham Nickel Alloys provides timely delivery of precision materials, offering bespoke solutions to suit the varied requirements of customers across industries.
| Standard Specification : | AMS 5759, AMS 5537 |
| Dimensions : | AMS, AMS, API |
| Sheets Thickness : | Range from .008″ to .0125″ |
| Plates Thickness : | Ranges from .0125″ to 5.00″ |
| Sheets/Plates Width : | 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc |
| Sheets/Plates Length : | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc |
| Tempers : | Annealed, 1/4, 1/2 Hard, 3/4 Hard, Full Hard |
| Hardness : | Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc. |
| Value Added Service : | Cladding, Heat T |
| Grade | C% | Si≤ % | Mn≤ % | P≤ % | S≤ % | Cr% | Ni% | Co% | Fe % | W % |
| Haynes 25 / L605 | 0.05-0.15 | 0.40 | 2.00 | 0.02 | 0.015 | 19.0-21.0 | 9.00-11.0 | Rest | ≤ 3.00 | 14.0-16.0 |
| Grade | 0.2% Yield strength Rp ≥ N/mm² | Tensile strength Rm N/mm² | Elongation A5 | Resistant on air up to°C | Modulus of elasticity kN/mm² |
| Haynes 25 / L605 | 345 | 830-1130 | 25 | 1090 | 225 |
Barsham Nickel Alloys is the biggest manufacturer and supplier of Haynes 25 / L605 Foil in Doha, Qatar. With high-quality, long-lasting, and corrosion-resistant products. Precision and reliability are ensured through our advanced manufacturing technology. We maintain industry standards and supply products on time with excellent customer service. Focused on quality and innovation, we supply reliable solutions to address the changing requirements of our customers.
Contact us to get a quick quote for your requirement.
Haynes 25 (L605) foil is extensively used in corrosive and high-temperature situations due to its considerable strength, oxidation resistance, and wear. It is used for afterburner parts, combustor liners, and turbine engine parts in the aerospace industry. It is used for orthodontic appliances and surgical implants by the medical sector due to biocompatibility. It also comes into play as an industrial gas turbine, furnace components, and heat exchanger component. Its sulfidation and oxidation resistance makes it suitable for chemical processing equipment. Haynes 25 is also utilized in springs, seals, and bearings for demanding applications involving superior mechanical properties at high temperatures.